Temper Grade

Hardness Guarantee (HR30T)

                                        Applications

Single Reduced 

T-1

49±3

Cans, nozzles, and other applications involving deep drawing that requires large flexibility

T-2

53±3

Items that require moderate drawability and some stiffness.

T-2.5

55±3

Items that require the drawability of T-2 in combination with the stiffness of T-3 for general uses.

T-3

57±3

Proper stiffness is imparted to prevent buckling. For general uses.

T-4

61±3

Can bodies, end and crowns that require comparatively large stiffness.

T-5

65±3

Can bodies, ends and other applications that require excellent buckling resistance.

Double Reduced

DR-8 

73±3

Bodies of carbonated beverage cans and beer cans that require stiffness and strength.

DR-9  

76±3     

Ends of carbonated beverage cans and beer cans that require stiffness and strength.

DR-9M

77±3    

The same as DR-9.

DR-10      

80±3

Special application that require strength.

                      T1-T5

                   DR8-DR10

Available Size Range

Size Range for Normal Production

Available Size Range

Size Range for Normal Production

Thickness

  (mm)  

   0.15-0.60

        0.18-0.50

   0.13-0.60

DR8     0.15-0.25

DR9     0.15-0.25

DR10   0.20-0.36

Width (mm)

   457-1067

         650-950

   457-1067

          690-950 

Length (mm)

   406-1110

         500-1050

   406-1110

          500-1050

Finish

Surface Roughness Aim Ra (*)

Features & Applications

Bright

0.25

Bright finish for general use.

Stone

0.40

Surface finish with stone marks that make scratches less conspicuous.

Super Stone

0.60

Surface finish with heavy stone mars.

Matte

1.00

Dull finish mainly used for making crown and DI cans (unmelted finish for tinplate)

Sliver (Stain)

/

Rough dull finish mainly used for making artistic cans (tinplate only, melted finish)

Type

                                              Description

 MR

Base steel low in residual elements that has excellent corrosion resistance.

It widely used in general applications.

  L

Base steel extremely low in residual elements such as Cu, Ni, Co, and Mo

that has excellent corrosion resistance to certain types of food

Products.

  D

Aluminum-killed base steel used in applications involving deep drawing or other types

of severe forming that tend to give rise to Lueder's lines.